Título : Diseño de mezcla para un concreto de alta resistencia adicionando Sika ViscoCrete SC-50 y GAIA
Autor : Roldán López, Lidmer Maurilio
Vargas Chávez, Joel Daniel
Asesor: Hurtado Zamora, Oswaldo
Palabras clave : Diseño de mezcla
Concreto de alta resistencia
Sika ViscoCrete SC-50
GAIA
Fecha de publicación : 2018
Institución : Universidad Privada Antenor Orrego - UPAO
No. de serie: T_ING.CIVIL_1563
Resumen : En la presente investigación se estudia los concretos de alta resistencia preparados con diferentes porcentajes de Nanosílice (GAlA NANOSILICE) (0.3%; 0.5%; 0.7%), en base a un concreto patrón (C.P) diseñada con un Superplastificante (viscocrete sc-50), en una dosis del 0.1% respecto al peso del cemento, el objetivo principal fue determinar en cuanto incrementa la resistencia mecánica a la compresión en diferentes dosis de Nanosílice adicionadas en base al Concreto Patrón. Para esto, se propuso diseñar mezclas de concreto según la metodología propuesta por el ACI 211.4 para las resistencias a la compresión de 420 y 600 kg/cm2, utilizando tres dosificaciones de aditivo nanosílice de 0.3%, 0.5% y 0.7% en peso de cemento para cada resistencia, y tomando en cuenta parámetros para los concretos con aditivo de 1 a 2 pulgadas según el ACI 211.4para los concretos patrón (sin aditivo), que sirvan para establecer propiedades del concreto como su trabajabilidad y consistencia. Después de tener las dosificaciones adecuadas, se procedió al preparado de cada una de estas, realizando los siguientes ensayos al concreto en estado fresco: asentamiento (Slump), temperatura, peso unitario volumétrico y porcentaje de aire; posteriormente se realizaron ensayos al concreto en estado endurecido: resistencia a la compresión a 3, 7 y 28 días de edad, como resultado del proceso de análisis de resistencia a la compresión se logró conocer la más óptima de aditivo Nanosílice la cual es de 0.5%. Para definir las dosificaciones de aditivo nanosílice y de Superplastificante se usó la recomendación del fabricante que establecía un rango de 0.5% a 3.0% y 0.5% a 1.8% respectivamente, las dosificaciones de los agregados se partieron según la metodología de diseño del comité ACI 211.4. Para 420 kgf/cm2 el contenido óptimo es 0.50% logrando resistencia de 448.10 kgf/cm2 Para 600 kgf/cm2 el contenido óptimo es 0.50% logrando resistencia de 637.60 kgf/cm2
In the present investigation, high strength concretes prepared with different percentages of Nanosilicate (GAlA NANOSILICE) (0.3%, 0.5%, 0.7%) are studied, based on a concrete pattern (CP) designed with a Superplasticizer (viscocrete sc-50), in a dose of 0.1% with respect to the weight of the cement, the main objective was to determine as it increases the mechanical resistance to compression in different doses of Nanosilica added on the basis of the Standard Concrete. For this, it was proposed to design concrete mixtures according to the methodology proposed by the ACI 211.4 for the compressive strengths of 420 and 600 kg / cm2, using three dosages of nanosilicate additive of 0.3%, 0.5% and 0.7% by weight of cement for each resistance, and taking into account parameters for concrete with additive of 1 to 2 inches according to the ACI 211.4 for the concrete pattern (without additive), which serve to establish concrete properties such as its workability and consistency. After having the appropriate dosages, we proceeded to the preparation of each one of these, performing the following tests on the concrete in fresh state: settlement (Slump), temperature, volumetric unit weight and percentage of air; Subsequently tests were performed on concrete in hardened state: resistance to compression at 3, 7 and 28 days of age, as a result of the compression resistance analysis process it was possible to know the most optimal Nanosilice additive which is 0.5%. To define the dosages of nanosilica additive and superplasticizer, the manufacturer's recommendation was used, which established a range of 0.5% to 3.0% and 0.5% to 1.8% respectively, the dosages of the aggregates were split according to the design methodology of the ACI 211.4 committee. For 420 kgf / cm2 the optimum content is 0.80% achieving resistance of 448.10 kgf / cm2. For 600 kgf / cm2 the optimum content is 0.80% achieving resistance of 637.60 kgf / cm2.
URI : https://hdl.handle.net/20.500.12759/4182
Aparece en las colecciones: Ingeniería Civil

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
REP_ING.CIVIL_LIDMER.ROLDAN_JOEL.VARGAS_DISEÑO.MEZCLA.CONCRETO.ALTA.RESISTENCIA.ADICIONANDO.SIKA.VISCOCRETE.SC50GAIA.pdfLIDMER.ROLDAN_JOEL.VARGAS_DISEÑO.MEZCLA.CONCRETO.ALTA.RESISTENCIA.ADICIONANDO.SIKA.VISCOCRETE.SC50GAIA3,46 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.