Título : Microfiltración IN VITRO en incrustaciones de resina compuesta empleando resina fotocurable precalentada y cemento resinoso dual autoadhesivo como agente de cementación
Autor : Ramirez Hidalgo, Gonzalo Rafael
Asesor: Villarreal Becerra, Einer Neils
Palabras clave : Microfiltración
In vitro
Fecha de publicación : 2018
Institución : Universidad Privada Antenor Orrego
No. de serie: T_ESTO_501
Resumen : Objetivo. Comparar el grado de microfiltración in vitro en circunstancias de resina compuesta empleando resina precalentada y cemento resinoso dual autoadhesivo como agente de cementación. Materiales y métodos. El estudio se realizó con 40 premolares, 20 premolares superiores y 20 premolares inferiores sanos, distribuidos al azar en grupo A y B. se realizaron cavidades expulsivas en M.O.D, luego se confeccionaron incrustaciones de resina para luego cementarlas. Al grupo A, fueron cementados con cemento resinoso dual autoadhesivo y el grupo B, con resina compuesta (3M Z250) precalentada a 65° C posteriormente las muestras fueron sumergidas en azul de metileno al 2% durante 24 horas, luego se lavaron, se secaron y se analizaron en un microscopio -estereoscopio con un aumento 40x. Los datos se procesaron en el programa estadístico SPSS versión 24.0 , para luego presentar los resultados en tablas de doble entrada y gráficos, se usó el test chi2. Conclusión: Se concluyó que si existe diferencias significativa en el grado de microfiltración in vitro entre el cemento resinoso dual autoadhesivo y la resina compuesta precalentada, siendo esta última mejor en el sellado marginal
Objective. To compare the degree of microfiltration in vitro under circumstances of composite resin using preheated resin and dual self- adhesive resinous cement as a cementing agent. Materials and methods. The study was performed with 40 premolars, 20 upper premolars and 20 healthy lower premolars, distributed randomly in group A and B. Ejection cavities were performed in M.O.D, then resin inlays were made and then cemented. Group A were cemented with self-adhesive dual resinous cement and group B with composite resin (3M Z250) preheated to 65 ° C subsequently the samples were immersed in 2% methylene blue for 24 hours, then washed, dried and they were analyzed in a microscope - stereoscope with a 40x magnification. The data were processed in the statistical program SPSS version 24.0, to then present the results in double entry tables and graphs, the chi2 test was used. Conclusion: It was concluded that there is a significant difference in the degree of in vitro microfiltration between the self-adhesive dual resinous cement and the preheated composite resin, the latter being better in the marginal sealing
URI : http://repositorio.upao.edu.pe/handle/upaorep/3776
Otros identificadores : T_ESTO_501
Aparece en las colecciones: Estomatología

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
RE_ESTO_GONZALO.RAMIREZ_MICROFILTRACIÓN.IN.VITRO_DATOS.PDFGONZALO.RAMIREZ_MICROFILTRACIÓN.IN.VITRO869,06 kBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.